羟基磷灰石(HA)表面改性对HA/聚乳酸复合材料力学性能的影响
Effect of surface modification of hydroxyapatite (HA) on the mechanical performances of HA/polyactic acid (PLLA)
【Author】 JIANG Yong-mei, JIANG Ping, WENG Jib School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, China
【机构】 西南交通大学材料科学与工程学院；
【摘要】 采用三种高分子有机物聚乙二醇(PEG)、聚乙烯醇(PVA)和聚丙烯酸(PAA)对羟基磷灰石(HA)颗粒表面进行改性处理,以便改善两相在复合时的界面结合强度,从而获得力学性能优良的复合材料.首先,将三种高分子聚合物分别溶于含HA颗粒的水溶液中,均匀分散后经喷雾干燥获得改性的粉体;然后,利用流延法获得HA/PLLA复合材料薄膜.研究了3种高分子表面改性HA颗粒后复合材料的力学性能,以及自然断面的界面结合情况.结果表明HA表面经PEG改性后,HA与PLLA间的界面结合状态优良,HA/PEG/PLLA的断裂强度较未经表面改性处理的HA颗粒与PLLA的复合材料的断裂强度提高了31%.
【Abstract】 Three polymers-polyethylene glycol (PEG)、polyvinyl alcohol (PVA) and polyacrylic acid (PAA), were selected to coat hydroxyapatite (HA) particles in an effort to improve the interface compatibility between HA particles and PLLA matrix in their composite, through the enhancement of the dispersion of filler particles in polymer matrix and the promotion of interfacial adhesion between these two phases. The mechanical performances were assessed by the tensile test and discussed on the basis of the interfacial morphologies. Significant improvements in the fracture strength were achieved in the case of the composite which was composed of PEG-coated HA particles and PLA.
【Key words】 hydroxyapatite； poly lactic acid； composite； surface modification； interfacial adhesion；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB332
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部