生物医用微孔高分子涂层的制备及其初始降解形貌的研究
Fabrication and primary degradation morphology of biomedical microporous polymer coatings
【Author】 XING Bin, ZHAO Hong, QI Min, LIU Lian, YANG Da-zhi (Dapartment of Materials Science and Technology, Dalian University of Technology, Dalian 116024, China)
【机构】 大连理工大学材料科学与工程系；
【摘要】 主要研究了316L不锈钢基体表面微孔聚丙交酯/乙交酯(PLGA)高分子载药涂层的制备技术,探索出空气湿度、温度、涂膜液的浓度等参数对涂层表面的孔径影响的规律,制备出孔径均匀的不锈钢表面PLGA涂层,并对微孔涂层在人工模拟体液(hank’s溶液)中的初始降解(3个星期)形貌进行了考察,从而为开发心血管介入治疗不锈钢支架上的微孔载药涂层技术奠定基础.
【Abstract】 The fabrication technology of microporous lactic/glycolic acid polymer (PLGA) coatings on 316L stainless steel matrix was studied in the paper. The effects of air humidity, temperature, concentration of the polymer solution on the diameter and density of the pores were investigated by scanning electron microscopy (SEM), and a coating homogeneous in size and distribution of the pores was formed on 316L stainless steel matrix. Furthermore, the primary degragation experiment of the microporous coatings in hank’s solution was carried out and the degradation morphology was described in the paper. The fabrication technology will be used to make microporous polymer drug coating on 316L stainless steel stents.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】R318.08
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部