退火对镀钽TiNi合金微观组织结构和血液相容性的影响
Effect of anncaling treatment on the microstructure and hemocompatibility of TiNi alloy coated with Ta
【Author】 CHENG Yan, CAI Wei, ZHENG Yu-feng, LI Hong-tao, ZHAO Lian-cheng (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
【机构】 哈尔滨工业大学材料科学与工程学院材料物理与化学系；
【摘要】 采用原子力显微镜(AFM)和X射线衍射分析(XRD)研究了退火处理对TiNi合金钽镀层微观组织结构的影响,研究表明:采用多孤离子镀在TiNi合金表面沉积得到了β-Ta镀层,经退火处理后,钽镀层的表面粗糙度增加,亚稳定的β-Ta相完全转变为稳定的α-Ta相.采用血小板粘附试验研究了退火对镀钽TiNi合金血液相容性的影响.发现经过退火处理后血小板粘附数量明显降低,血小板没有发生聚集和变形,只有少数长出了伪足,即血小板基本未被激活,说明退火改善了镀钽TiNi合金的血液相容性.
【Abstract】 The effect of annealing treatment on the microstructure of tantalum coatings deposited on the TiNi alloys was investigated by atomic force microscopy (AFM) and X-ray diffraction analysis (XRD). The results show that the surface roughness increase and the metastable β -Ta transform to α-Ta after annealing treatment. The effect of annealing treatment on the hemocompatibility was studied by the platelet adhesion test, it has been found that the amount of platelet adhered on the annealing sample decrease significantly compared to that of the as-deposited sample, in addition, no sign of accumulation and only slight pseudopodium is observed on the sample, suggesting that the annealing treatment can improve the hemocompatibility of TiNi alloy.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG156.2
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部