温敏性壳聚糖/甘油磷酸盐配合物凝胶的研究
Properties of thermo-sensitive hydrogels based on a chitosan/glycerophosphate salts complex
【Author】 WU Yan, QU Bo, ZHAO Jin, KUANG Qing-lin, CHENG Guo-xiang (School of Material Science and Engineering, Tianjin University, Tianjin 300072, China)
【机构】 天津大学材料科学与工程学院；
【摘要】 采用壳聚糖与甘油磷酸盐分子组装的原理制备了具有温敏性的配合物凝胶体系,其在室温下呈液态,升温凝胶化.研究结果表明,α-甘油磷酸钠(α-GP)与β-甘油磷酸钠(β-GP)按一定比例混合与壳聚糖配合的体系,具有较宽的调节IGT的能力,可在更短的时间内凝胶,并且凝胶强度增大.当α-GP的混入比为30%w/w时,与未加入α-GP的体系相比,凝胶体系IGT可由37℃降低至29℃,并且体系在37℃下,可在200s内快速凝胶,强度可达到约0.51kPa.
【Abstract】 Thermo-sensitive neutral systems based on a chitosan/glycerophosphate salt complex were prepared. Various factors that affected the propenies of gels were tested, including component concentrations, the molecular vveight and the degree of deacetylation of chitosan, and the percentage of α-GP in the GP, etc. Compared with the formulations using only disodium- β -glycerophosphate (β -GP), the systems based on chitosan/glycero- phosphate salt (GP, the mixture of disodium- α -glycero-phosphate (α -GP) and disodium- β -glycerophosphate (β -GP)) could turn into gels at a lower temperature. The results showed that the incipient gelation temperature (IGT) of the formulations was shifted from 37℃ to 29℃, when β-GP was substitued partially by α-GP by 30%w/w. They could form gels in 200s at 37℃C with the gel strength reaching about 0.51KPa.
【Key words】 chitosan； glycerophosphate salt； molecular assembly； comples hydrogels；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】R318.08
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部