聚酰胺-胺型树枝状分子的合成及其水溶液表面张力的研究
Synthesis of poly(amidoamine) and its surface tension in water solution
【Author】 HUANG Fei, XU Liang-hua, XU Hai-yan(School of Materials Science and Engineering, Beijing University of Chemical Technology, Beijin 100029, China; School of Basic Medicine, CAMS & PUMC, Beijing 100005, China)
【机构】 北京化工大学材料科学与工程学院； 中国医学科学院中国协和医科大学基础医学部；
【摘要】 实验合成了以乙二胺(EDA)为核的1.0-3.0代聚酰胺-胺型树枝状分子,对合成的产品进行了核磁、红外、元素分析等表征.采用Wilhelmy吊板法测定了整代1.0-3.0代不同浓度下聚酰胺-胺型树枝状分子水溶液的表面张力,探讨了不同代数聚酰胺-胺型树枝状分子的表面活性。实验表明:整代聚酰胺-胺型树枝状分子表面活性很小,但是2.0代分子水溶液的表面张力比同浓度的1.0代和3.0代分子水溶液的表面张力都低,而不是按由低代到高代的顺序递减.
【Abstract】 A series of EDA core based poly(amidoamine) from 1.0 to 3.0 Generation are synthesized and characterized with 139C-NMR, IR, Elemental Analysis etc. Wilhelmy measure plate method is taken to measure the surface tension of poly(amidoamine) from 1.0 to 3.0 in water solution, the variety in surface tension of different generation matching with the variety of concentration are studied. It can be observed in experiment that among the generations from 1.0 to 3.0, the 2.0 generation poly(amidoamine) has a higher surface activity than 1.0 and 3.0 generation. But overall, 1.0,2.0,3.0 generation poly(amidoamine) show little surface activity.
【Key words】 poly(amidoamine)； surface tension； wilhelmy measure plate method；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】O631
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部