AZ91D镁合金阻尼性能的研究
Study on damping capacity of AZ91D magnesium alloys
【Author】 HU Xiao-shi, ZHANG Yong-kun, ZHENG Ming-yi, WANG Yan-qiu, WU Kun (School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
【机构】 哈尔滨工业大学材料科学与工程学院；
【摘要】 利用动态机械分析仪(DMA)研究了热处理工艺对商业AZ91D镁合金阻尼性能的影响规律.研究结果表明:热处理对AZ91D镁合金的阻尼性能有较明显的影响.时效处理态AZ91D镁合金的临界脱钉应变振幅小于固溶处理态.当应变振幅大于临界应变振幅,合金的阻尼值迅速升高.随着测试温度的升高,合金的阻尼值升高,在临界温度之前以位错阻尼机制为主,当温度超过临界温度则以晶界滑动为主要阻尼机制.
【Abstract】 The effect of heat treatment on damping capacity of commercial AZ91D Magnesium alloys were studied by dynamic mechanical analyzer (DMA). It showed the damping capacities of experimental materials were obviously influenced by heat treatment methods. The aged samples showed the minimum critical strain amplitude than solution treated one and the damping capacities were rapidly increase when exceeded the critical strain amplitude. The damping capacities of these samples were increase with the increasing of test temperature. The main damping mechanism before critical temperature was dislocation movement and after that was grain boundary gliding.
【Key words】 heat treatment methods； AZ91D magnesium alloy； damping capacity；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG113.22
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部