乙醇对金刚石膜生长特性的影响
Effect of ethanol on diamond film growth
【Author】 LI Chun-yan, JIN Zeng-sun, LU Xian-yi (National laboratory of Super Hard Materials of Jilin University, Changchun 130012, China)
【机构】 吉林大学超硬材料国家重点实验室；
【摘要】 采用EA-CVD(Electron Assisted Chemical VaporDeposition)方法制备金刚石厚膜,在反应气体(CH4+H2)中添加乙醇,在保持其它条件不变的情况下研究了不同乙醇流量对金刚石膜生长的影响.利用拉曼光谱和SEM等测试方法对金刚石膜进行了表征,证实乙醇电离时产生的氢氧键对金刚石有很强的刻蚀作用.在沉积过程中向系统中加入乙醇对金刚石膜表面形貌有显著的影响,适量的乙醇有利于提高膜品质和生长速率,但过量的乙醇会导致对金刚石表面的刻蚀加剧,使金刚石膜的生长受到抑制.
【Abstract】 Diamond thick films were synthesized by EA-CVD with hydrocarbon compound gases (CH4/C2H5OH/H2). The influence of ethanol concentration on diamond fllms growth was investigated using Raman and SEM. It was validated that -OH boned, which was generated by decomposed ethanol in the glow discharge process, has a strong ability to etch diamond. Results show that proper ethanol concentration is of advantage to the improvement of the quality and the increase of the growth rate of diamond films during the deposition. The surface of diamond films is obviously etched and the growth rate of diamond films is restricted when the ethanol concentration is too high.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】O484.1
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部