脂肪酸修饰多壁碳纳米管及其摩擦性能研究
Modification of carbon nanotubes with fatty acid and their tribological properties
【作者】 陈传盛； 陈小华； 张华； 胡静； 许龙山； 杨植； 林良武；
【Author】 CHEN Chuan-sheng, CHEN Xiao-hua, ZHANG Hua, Hu Jing, XU Long-shan, YANG Zhi, LIN Liang-wu (College of Materials Science and Engineering, Hunan University, Changsha 410082, China)
【机构】 湖南大学材料科学与工程学院；
【摘要】 采用硫酸和硝酸混合酸对催化裂解法(CVD法)制备的多壁碳纳米管(MWNTs)进行纯化,然后运用硬脂酸对碳纳米管表面进行修饰,并研究了硬脂酸修饰后的碳纳米管的表面状况以及作为润滑油添加剂的摩擦学行为.实验结果表明,在硫酸催化剂作用下,通过化学反应碳纳米管能够被硬脂酸包覆,而且硬脂酸修饰的碳纳米管作为润滑油添加剂能够显著提高成品油的减摩抗磨性能.在1000N载荷下硬脂酸在成品油中的质量百分比为0.4%和多壁碳纳米管质量百分比为0.15%-0.2%时,成品油的摩擦学性能最佳。
【Abstract】 The Mutli-walled carbon nanotubes were modified with stearic acid by chemical reactivity. The tribological behavior of stearic acid coated carbon nanotubes as lubricant additive were investigated. The results show that the surface of carbon nanotubes was coated with a modified layer of stearic acid, and the modified carbon nanotubes could be dispersed in lubricant uniformly. Moreover, the modified carbon nanotubes as lubricant additive effectively improved the friction-reduction and anti-wear ability of lubricant. The optimum contents of MWNTs and stearic acid in lubricant is 0.15-0.2% and 0.4%, respectively.
【Key words】 carbon nanotubes； surface modification； dispersion: tribological property；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部