高阻尼TiNi合金
High-damping TiNi alloy
【Author】 ZHANG Xiao-ming, TAN Shuan-bin, WANG Li-xin, WANG Xiao-peng, WANG Xue-cheng (Northwest Institute for Non-ferrous Metai Research, Xi’an, 710016, China;Collage of Mechanical Engineering, Xi’an Jiaotong University, Xian 710049, China;Shaoxing Yuexiu Foreign College of Vocational Education, Shaoxing 312000, China)
【机构】 西北有色金属研究院陕西； 西安交通大学机械工程学院； 绍兴越秀外国语职业学院；
【摘要】 等原子比的TiNi合金除具有独特的形状记忆效应、超弹性效应和良好的耐磨耐蚀性外,还有着优异的阻尼性能,为当前几种最著名的高性能减振合金之一.用自蔓延高温合成(燃烧合成)法制备了孔洞发达、形状不规则、相对孔隙度50%左右的多孔TiNi合金.多孔体密度为3.15g/cm3,压缩强度270MPa,压缩变形率20%,压缩弹性模量2.5GPa.其阻尼性能比相同成分的致密TiNi合金提高了50%以上,对振动的衰减比致密TiNi合金高一个数量级.
【Abstract】 TiNi alloy with equal atom ratio is a type of vibration damping alloy with perfect performance because of its good damp property besides special shape-memory effect, super-elasticity effect, perfect wear resistance and corrosion-resistant. The samples with more non-regular pores, relative porosity 50%, are prepared by the self-propagating high-temperature synthesis process. This alloy is possessed of the following characteristics: density 3.15 g/cm3, compression strength 270MPa, compression deformation 20%, compression e!asticity modulus 2.5GPa. The damp property of this alloy is 1.5 times than that of dense TiNi alloy and 10 times for vibration fading.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅱ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG135
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部