合金包覆空心微珠粉体吸波材料的制备
Preparation of Ni-Co-P alloys-coating of cenosphere particles
【Author】 XU Jian, XIONG Wei-hao, ZENG Ai-xiang, WANG Cai-fang(State Key Laboratory of Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, China; Department of Chemistry, Changsha University of Science and Technology, Changsha 410077, China)
【机构】 华中科技大学模具技术国家重点实验室；
【摘要】 采用粉体化学镀技术,以AgNO3取代常见的贵金属盐PdCl2作为活化剂、H2PO2取代Sn2+作为还原剂,经一步前处理过程,在空心微珠表面包覆NiCOP合金.利用扫描电镜、能谱分析仪分别讨论包覆层的形貌和成分,表明NiCoP合金均匀包覆在空心微珠表面:X射线衍射和磁强计分析表明,未经热处理的包覆合金涂层为非晶态结构,无明显的铁磁性:经热处理后的包覆合金涂层转变为晶态结构,表现出较强的铁磁性,有利于吸收电磁波.最后,提出了这种改进工艺的一种可能的机理.
【Abstract】 Electroless NiCoP alloys-coating of cenosphere particles by one-step pre-treatment was demonstrated in the present investigation. AgNO3 was used as activator to replace the conventional PdCl2 activator and H2PO2 was used to replace Sn2+ as the reducing agent. The SEM and EDX analysis showed that NiCoP alloys uniformly covered the surface of the cenosphere particles under the given coating conditions. The XRD analysis indicated that the coating alloys were amorphous, therefore, having no ferromagnetism while they changed to be crystal and had somewhat ferromagnetism after the coated cenosphere particles being heat-treated. The possible mechanism of electroless NiCoP alloys-coating of cenosphere particles was suggested.
【Key words】 fly ash cenospheres； powder electroless； nicop alloy； pre-treatment technique； radar absorption materials；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部