钆颗粒的制备及性能研究
The preparation and property of gadolinium sphere and granule
【作者】 张泽玉； 闻达； 王东； 龙毅； 叶荣昌； 万发荣；
【Author】 ZHANG Ze-yu, WEN Da, WANG Dong, LONG Yi, YE Rong-chang, WAN Fa-rong (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)
【机构】 北京科技大学材料学院；
【摘要】 采用两种不同方法制备了钆球与钆颗粒,并对两种材料的磁性能进行了研究.结果表明,由于机加工带来的应力应变及不规则尺寸,导致钆颗粒的磁性能不同于钆球。首先,机加工制备的颗粒,尽管其氧含量比加工前高出一倍,而离心雾化法制得的钆球氧含量基本不变,钆颗粒与钆球的最大磁熵变相差不大;其次,钆颗粒与钆球的居里温度存在偏差,分别为293K和296K:再者,在相同磁场下,居里温度以上温区,钆颗粒的磁熵变趋于平缓,且大于钆球的磁熵变,这种趋势在高磁场下更为明显。
【Abstract】 In this paper, gadolinium (Gd) sphere and granule are prepared by different ways. Magnetization measurements on the Gd sphere and granule indicate that the magnetocaloric effects are different for the different processing of the ingot material into sphere and granule. Firstly, the oxide content of Gd granule is two times than ingot material, but its maximum magnetic entropy change is as same as that of Gd sphere, which remains the same oxide content with ingot material. Secondly, Gd granule has a higher Curie temperature than Gd sphere, 296 vs 293. Thirdly, the magnetic entropy change of Gd granule is smoother and higher than that of Gd sphere over the Curie temperature. The trend is evident in high magnetic field.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB64
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部