杂质分布对稀土金属钆水中腐蚀性能的影响
The influence of impurity distribution to the corrosion rate of gadolinium in water
【作者】 张泽玉； 闻达； 吴磊； 龙毅； 叶荣昌； 万发荣；
【Author】 ZHANG Ze-yu, WEN Da, WU Lei, LONG Yi, YE Rong-chang, WAN Fa-rong (School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)
【机构】 北京科技大学材料学院；
【摘要】 作为磁制冷工质的稀土金属钆(Gd),由于长期处于热交换介质水中,而钆本身化学稳定性差,室温下即可与水发生析氢反应,所以钆在水中的腐蚀行为研究对磁制冷机的开发有着重要意义.通过失重法、极化曲线法、扫描电镜观察及X-射线能谱分析表明,杂质含量相近、杂质细小且弥散均匀的金属,与杂质较大但集中分布的金属相比,腐蚀严重.
【Abstract】 Gd usually works in water medium used as heat transfer fluid in most successful magnetic refrigerators. However, the poor corrosion resistance of Gd in water affects the potential for its applications. In this study, the corrosion behaviors of Gd in different water were investigated by weight loss and electrochemical measurements. The results show that the corrosion rate of Gd in deionized water is much lower than in tap water for the absence of anion in deionized water. The distribution of impurity in metal Gd has an important influence on the corrosion rate.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG174
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部