退火过程对非晶FeGeB合金磁性的影响
Effect of thermal treatment on the magnetic properties of amorphous FeGeB alloys
【Author】 MAO Xing-yu, XU Feng, GAO Wen-li, TANG Jian-chen, DU You-wei(National Laboratory of solid State Microstructure, Department, of Physics, Nanjing Univ. Nanjing 210093, China; Institute of Science, Jimei Univ, Xiamen 361021, China)
【机构】 南京大学物理系固体微结构实验室；
【摘要】 用单辊急冷法制得的FeGeB非晶条带,经退火处理后,发现其软磁性能下降.实验表明,在退火过程中有粗晶粒的Fe3Ge相形成,而没有观察到α-Fe相.由于Fe3Ge的晶粒尺寸超过铁磁交换作用长度,晶粒间各向异性常数不再相互抵消,引起了磁晶各向异性的增加,从而导致了样品的磁导率下降和矫顽力的上升.
【Abstract】 The magnetic properties of amorphous Fe-Ge-B alloy before and after thermal treatment are investigated. Unlike nanocrystalline alloys, the annealed amorphous Fe73Ge20B7 alloy experiences a magnetic hardening rather than softening. The permeability is halved and the coercivity is increased greatly. Coarse-grained Fe3Ge metallic compound is observed after annealing. The size of Fe3Ge crystallites exceeds the exchange interaction length, resulting a failure of averaging out of effective anisotropy.
【Key words】 amorphous alloy: nanocrystalline； crystallization； magnetic property； metallic compound；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TG156
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部