掺杂稀土元素镧的钡铁氧体超微粉末的微波吸收特性研究
Study on microwave-absorption properties of rare earth La doped barium ferrite supper-powders
【Author】 YUN Yue-hou, ZHANG Chang-zai, LI Guo-dong (Department of Physics, Inner Mongolia University, Hohhot 010021, China)
【机构】 内蒙古大学物理系；
【摘要】 采用溶胶-凝胶法制备了掺杂稀土元素镧的钡铁氧体超微粉末,就镧元素的掺杂含量对钡铁氧体吸波性能的影响进行了对比研究。实验表明,用聚乙二醇凝胶法制备的BaLaxFe12-xO19超微粉末,当x为0.03时,对微波吸收效果最佳。在涂层厚度1.0mm,测试频段为7.5-11.9GHz内,吸收量均在25dB以上,在11.6GHz处,吸收峰值达41.4dB。
【Abstract】 In this paper, BaLaxFe12-xO19 supper-powders were prepared by sol-gel technique. The effect of different amount of Lanthanum on supper-powders’ microwave-absorption properties was discussed. The result indicates that BaLaxFe12-xO19 (x=0.03) sample has the best microwave-absorption properties. The absorption quantity of BaLa0.03Fe11.97O19 for a coat thickness of 1.0mm is over 25dB in the frequency range of 7.5-11.9 GHz. The absorption peak of 41.4dB at 11.6 GHz is found.
【Key words】 sol-gel method； rare earth； barium ferrite； supper-powder； microwave-absorption properties；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部