用精铁矿粉代替铁红制备功率软磁铁氧体的实验研究
Research on the preparation process of the power soft-ferrite using the refined iron-mineral powder in place of Fe2O3
【Author】 YAO Xue-biao, HU Guo-guang, YIN Ping (Department of Physics, Anhui University, Hefei 230039, China)
【机构】 安徽大学物理及材料科学学院；
【摘要】 用精铁矿粉(Fe3O4)代替铁红(Fe2O3)制备功率软磁铁氧体是一项开拓价廉量富原材料的高技术和高效益应用的创新研究课题。本文介绍了其中因代替原材料的成分不同及含SiO2杂质量较高等引起的氧化物制备工艺中面临新的技术关键和难点所进行的实验研究。结果不仅在实验室中用Fe3O4代替Fe2O3和Mn3O4代替MnCO3研制出功率MnZn铁氧体样品,而且在现有的小型企业生产线上中试生产出合格的功率软磁铁氧体元件产品。
【Abstract】 The preparation of the power soft-ferrite using the refined iron-mineral powder, that is Fe3O4 is a new studied item, Which deals with the substitution of the raw material with low cost and rich source in high benefit and new technology .Because the composition of Fe3O4 is different from Fe2O3 and the content of impurities such as SiO2 and so on is higher in Fe3O4, the experimental research on key technics and difficulty problems in oxide-prepared process was reported in the paper.The experimental results show that not only the samples of the power MnZn ferrite were prepared on a small scale in our experiment room and its elements are manufactured on medium scale in factory.
【Key words】 refined iron-mineral powder； substitution； MnZn ferrite； power； preparation process；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM271
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部