PM法制备Sm2Fe17Nx永磁材料最佳工艺的研究
Study on fabrication technology of Sm2Fe17Nx permanent magnetic powders with high magnetic performance
【Author】 ZHANG Dong-tao, JI Yong-cheng, YUE Ming, ZHANG Jiu-xing(The Key Laboratory of Advanced Functional Materials, Ministry of Education,Beijing University of Technology, Beijing 100022, China)
【机构】 北京工业大学新型功能材料教育部重点实验室；
【摘要】 采用粉末冶金工艺制备了各向异性Sm2Fe17Nx永磁粉末。重点考查了工艺参数对Sm2Fe17合金的显微组织及Sm2Fe17Nx粉末磁特性的影响。结果表明,铸态合金的均匀化、粉末的氮化以及粉碎过程是获得高性能磁粉的关键因素。采用优化工艺条件制备的磁粉的磁特性为:Jr=1.24T,iHc=756kA/m,(BH)max=220kJ/m3。
【Abstract】 Anisotropic Sm2Fe17Nx permanent magnetic powders were prepared by powder metallurgy technique. Effects of processing conditions on the microstructure of Sm2Fe17 alloy as well as the magnetic properties of Sm2Fe17Nx magnetic powders were studied. Magnetic properties, microstructure and constituents of the alloy and powders were investigated using X-ray diffraction, scanning electron microscope and vibrating sample magnetometer. It is found that the magnetic performance of the powders mainly depended on the process of homogenization, nitrogenation and pulverization which are the key fabricating technologies for preparing the magnetic powders. Adopting optimal processing conditions, we prepared the powders with magnetic properties of Ji= 1.24T, iHc=756kA/m and (BH)max=220kJ/m3.
【Key words】 permanent magnetic powders； Sm2Fe17Nx； homogenization； nitrogenation； pulverization；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TM273
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部