(FeCo)73.5Cu1Nb3Si15.5B7纳米晶合金晶化过程的研究
Study on the crystallization of （FeCo）73.5Cu1Nb3 Si15.5B7 nanocrystalline alloy
【Author】 ZHI Qi-zheng, WANG Ji-jie, Liu Wei-de, CHEN Wen-zhi(School of Materials & Metallurgy, Northeastern University, Shenyang 110004, China; National Amorphous & Nanocrystalline Alloy Engineering Research Center, Central Iron & Steel Research Institute, Beijing 100081, China)
【机构】 东北大学材料与冶金学院； 钢铁研究总院国家非晶微晶工程技术研究中心；
【摘要】 采用四探针法和X射线衍射技术研究了(FeCo)73.5Cu1Nb3 Si15.5B7合金在定速升温过程相对电阻率与结构的变化。实验发现在电阻率快速上升的温度范围与晶化的第一阶段有关,是由纳米尺寸bcc的α-Fe(Si)固溶体形成引起的。在晶化发生的第二阶段,剩余非晶相转变为硼化物(Fe3B和Fe23B6)相,电阻率有所下降。
【Abstract】 The variation in the relative electrical resistivity and structure of (FeCo)73.5Cu1Nb3 Si1505B7 Alloy during constant-rate heating were studied by four-probe dc measurements and X-ray diffraction. It was found that the region where the electrical resistivity goes up rapidly are associated with the first stage of crystallization, corresponding to the development of the nanosized bcc α-Fe (Si) solid solution. When the second stage of crystallization takes place, involving the transformation of the remaining amorphous phase into a mixture of boride phases (Fe3B and Fe23B6), a definite drop of the electrical resistivity appears.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部