铁基纳米晶合金条带在低频低场下磁化机制的磁谱研究
The mechanism of magnetic relaxation in fe-based nanocrystalline alloy ribbons investigated by permeability spectroscopy
【Author】 XU Feng, QIN Wen, PENG Kun, DU You-wei(National Key Laboratory of Solid State Microstructure, Department of Physics, Nanjing University, Nanjing210093, China;Research Institute for Micro/Nanometer Science and Technology, Shanghai Jiao Tong University,Shanghai 200030, China; Department of Material Physics, Hu’nan University, Changsha 410082, China)
【机构】 南京大学固体微结构国家重点实验室； 上海交通大学微纳米科技研究中心； 湖南大学材料物理系；
【摘要】 利用磁谱研究了铁基纳米晶合金条带在低频低场下的动态磁化性能对条带厚度的依赖性,从而探讨了其磁化机制。实验结果和基于畴壁振动方程的解释充分一致,证实了被钉扎的畴壁振动是在低频低场下该种材料的主导磁化机制。
【Abstract】 In the present work, in order to elucidate the mechanism of magnetic relaxation in Fe-based nanocrystalline alloy ribbons at low fields and low frequencies, the dependence of the dynamic magnetization properties of nanocrystalline alloy ribbons on the thickness of ribbons has been investigated by permeability spectroscopy. The agreement of the experimental results with the domain wall motion equations confirms that domain wall bulging between the pinning edges is the dominant magnetization mechanism at low fields and low frequencies.
【Key words】 nanocrystalline soft magnetic material； magnetic permeabilty spectra； domain wall；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部