含偶氮苯侧链的新型三阶非线性聚炔材料的制备及性能
Synthesis and properties of polyacetylene having azobenzene pendant group
【Author】 YIN Shou-chun, GUANG Shan-yi, XU Hong-yao, ZHOU Jian-ping (Anhui University, Faculty of Chemistry and Chemical Engineering, Hefei 230039, China)
【机构】 安徽大学化学化工学院；
【摘要】 我们以中等产率成功的合成出一种含偶氮苯功能基团的、可溶解的、立体规整的、中等分子量的聚炔高分子.采用五步法合成了新颖的偶氮苯乙炔单体,2-[N-甲基-N-4-[(4-乙炔苯基)偶氮苯基]氨基]乙基丁酸酯.使用[Rh(nbd)Cl]2-Et3N将单体进行了聚合.采用FT-IR,UV-vis,GPC和NMR等对得到的聚炔高分子分子结构进行了表征。在8ns脉宽波长532 nm激光下采用Z-扫描技术对聚合物的溶液进行了非线性光学性能的测试.
【Abstract】 The new azoacetylene monomer, 2-[N-methyl-N-4-[(4-ethynylphenyl)azo]phenyl]amino]ethyl butyrate was synthesized via five step reactions. The monomer was polymerized by [Rh(nbd)Cl]2-Et3N to get the soluble, stereoregular, and moderate molecular weight polyacetylenes containing azobenzene functional groups in moderate yields. The polymer was characterized by FT-IR, UV-vis, GPC and NMR and its nonlinear optical property was measured using Z-scan technique at 532 nm wavelength with 8 ns pulse width.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB34
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部