YAG:Er3+粉体的sol-gel燃烧法合成与上转换发光研究
Synthesis of YAG: Er3+ powders by sol-gel combustion process and its upconversion luminescence
【Author】 LIU Min, WANG Shi-wei, ZHANG Jian, AN Li-qiong, CHEN Li-dong (Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China)
【机构】 中国科学院上海硅酸盐研究所；
【摘要】 以柠檬酸作为络合剂和燃料,用sol-gel燃烧法,制备了(Y1-xErx)3Al5O12粉体(x=0.001、0.005、0.01、0.05、0.1).在800℃,粉体直接由无定形相转变为YAG单相.采用980nm的半导体激光器激发,YAG:Er3+发出较强的红绿光.且有两个主发射峰552.5nm和675nm.随着掺杂量的增加,发光强度先增加后减小,当Er3+掺杂量为5%(x=0.05)时,上转换发光强度最大.另外,对其上转换发光机制进行了讨论.
【Abstract】 (Y1-xErx) 3A15O12 powders with x=0.001, 0.005, 0.01, 0.05, 0.1 were prepared by sol-gel combustion process. Amorphous precursor transformed directely into pure YAG phase at 800℃. YAG:Er3+ powders emitted green and red light pumped by a 980nm continuous wave diode laser, and the two main emission peaks centered at 552.5nm snd 675nm, respectively. The intensity of luminescence firstly increased and then decreased when Er3+ doped increased, and it reached maximum when 5% Er3+ was doped. The mechanism of luminescence was also discussed.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB44
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部