纳米La2O3:Eu的结构及其光致发光性质研究
Structure and photoluminescence of nanocrystalline La2O3:Eu
【Author】 FU Xiao-yan.NIU Shu-yun, ZHANG Hong-wu, XIN Qin(College of Chemistry and Chemical Engineering, Liaoning Normal University, Dalian 116029, China; Dalian Institute of Chemical Physics , Chinese Academy of Sciences, Dalian 116023, China)
【机构】 辽宁师范大学化学化工学院； 大连化学物理研究所；
【摘要】 采用共沉淀法制备出蚋米级La2O3:Eu.并采用相关光谱、X-射线衍射(XRD)、荧光光谱(PL)对所制备的纳米发光粉体进行表征.结果表明:制备的纳米发光粉体的粒径均匀,集中在20nm左右:XRD结果证明制备的La2O3:Eu粉体属于六方相,PL的结果说明La2O3:Eu具有良好的发光性质.
【Abstract】 A simple co-precipitation was introduced to prepare nanocrystalline La2O3:Eu. The powder was characterized by X-ray diffraction(XRD), granularity analysis and photoluminescence(PL). The results of XRD and granularity analysis show that high-quality nanopowders with controlled particle size(20nm) were prepared at a relatively low temperature about 700℃. Upon UV excitation this phosphor exhibit excellent red luminescence. Due to the absence of an inversion symmetry at the Eu3+ lattice site (C3 symmetry), the intensity of force electric-dipole transitions 5D0-7F2.4 is strong while that of 5D0-7F1.3, magnetic dipole transitions is relatively weak.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB383
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部