La0.8Sr0.2CoO3的拉曼光谱特性研究
The Raman spectroscopy of Lao.gSr0.2CoO3
【Author】 WANG Ji-you, WANG Jun-ling, HE Hong, JIANG Shao-lin, HOU Bi-hui ( College of Applied Sciences, Beijing University of Technology, Beijing 100022, China: College of Environmental and Energy Engineering, Beijing University of Technology, Beijing 100022, China)
【机构】 北京工业大学应用数理学院； 北京工业大学环境与能源工程学院；
【摘要】 采用柠檬酸盐法制备了斜方六面体型(rhombohedral)钙钛矿材料La0.8Sr0.2CoO3,测量了它的拉曼光谱,我们发现随着测量用激光的激发功率的增加,705cm-1附近的拉曼振动峰不断移动,且拉曼峰的强度也不随激发功率的增加而线性增加,当激发功率达到1.5mW时,材料出现荧光,随激发光增强,荧光快速增大,同时拉曼峰消失.
【Abstract】 La0.8Sr0.2CoO3 was prepared by a citrate method. X-ray diffraction pattern indicates an almost pure rhombohedral phase. Raman spectroscopy was measured by using micro-Raman spectrometer in different laser intensities. It is found that the Raman peaks shift with increasing the laser power. It indicates that the structure of La0.8Sr0.2CoO3 transformed with increase of the intensity of laser irradiation.
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】TB33
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部