掺Mn近化学计量比铌酸锂晶体生长及其性质
Growth and properties of MnO doped near stoichiometric LiNbO3 crystals
【Author】 SUN Zhi-jie, LI Hong-tao, YE Shao-jian, CAI Wei, ZHAO Lian-cheng (School of Material Science and Engineering, Harbin Institute of Technology, Harbin 150001, China)
【机构】 哈尔滨工业大学材料科学与工程学院；
【摘要】 采取中频加热和TSSG的方法,从掺入了6%(质量分数)K2O的同成分Li2O-Nb2O5熔体中生长出了近化学计量比铌酸锂单晶,其铁电畴结构为单畴结构,居里温度为1191.5℃.在此基础上,分别掺入0.05%(质量分数),0.16%(质量分数)和0.32%(质量分数)的氧化锰,生长了掺Mn近化学计量比的铌酸锂晶体,其铁电畴结构也均为单畴结构,居里温度分别为1195.3、1201.5和1219℃.对这4个晶体进行的红外光谱测试的结果表明:均在3466cm-1有一吸收峰。通过二波耦合实验,我们对不同掺杂浓度的4种晶体进行了光折变性能测试.
【Abstract】 In this paper, the SLN crystals doped with different concentration of Mn ions have been grown by the top seeded solution growth (TSSG) method by adding K2O flux to Li2O-Nb2O5 melt. The crystals showed single domain structures, and their Curie temperatures is 1191.5, 1195.3, 1201.5 and 1219℃, respectively. The crystal structures were analyzed by 1R spectra. The photorefractive properties of SLN were experimentally studied by using two-beam coupling. From the writing and erasure curves, writing time, erasure time, and diffraction efficiency of the crystals were measured.
【Key words】 Mn-doped SLN； TSSG； photorefractive properties； two wave coupling；
- 【会议录名称】 第五届中国功能材料及其应用学术会议论文集Ⅰ
- 【会议名称】第五届中国功能材料及其应用学术会议
- 【会议时间】2004-09
- 【会议地点】中国北京·秦皇岛
- 【分类号】O782
- 【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部