双掺铈锰铌酸钾锂晶体的生长及光折变性能的研究

The growth and photorefractive properties of Ce:Mn:KLN crystals

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 LIU Bo, BI Jian-cong, ZHENG Wei, XU Yu-heng( School of Chemistry and Environment Engineering, Harbin University of Science and Technology, Harbin 150040, China; Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001, China)

【机构】哈尔滨理工大学化学与环境工程学院；哈尔滨工业大学应用化学系；

【摘要】在铌酸钾锂（KLN）中掺进CeO₂和MnCO₃,采用Czchralski法首次生长Ce:Mn:KLN晶体,测试晶体的晶格常数,Ce:Mn:KLN晶体的晶格常数变小.测试晶体的吸收光谱,它的吸收边相对KLN晶体发生红移.研究晶体吸收边发生红移的原因.以二波耦合光路测试Ce:Mn:KLN晶体的指数增益系数Γ.它的指数增益系数最大值Γmax=9.2cm～1,大于KLN晶体的Γ值.更多还原

【Abstract】 Doped with CeO₂ and MnCO₃, Ce:Mn:KLN crystals were grown by Czchralski method for the first time. The crystal lattice constants were measured, the crystal lattice constant of Ce:Mn:KLN decreased in compared with that of KLN. The UV absorption spectra of those crystals were measured. The absorption edges of Ce:Mn:KLN shift to the longer wavelength compared to that of KLN. The mechanism of shifting was reaserached. The exponent gain coefficient of Ce:Mn:KLN was measured by using two-wave coupled light path, the maximum （Γmix=9.2cm-1） is larger than that of KLN.更多还原

【关键词】铌酸钾锂；光折变性能；晶格常数；
【Key words】 KLN； photorefractive properties； lattice constants；

【基金】 973项目(G19990330);863项目(2001AA31304)

【会议录名称】第五届中国功能材料及其应用学术会议论文集Ⅰ

【会议名称】第五届中国功能材料及其应用学术会议

【会议时间】2004-09
【会议地点】中国北京·秦皇岛
【分类号】O782

【主办单位】国家仪表功能材料工程技术研究中心、国家“863”计划新材料领域专家委员会、中国仪器仪表学会仪表材料学会、中国金属学会、中国稀土学会、中国复合材料学会、中国有色金属学会、重庆仪表材料研究所、北京有色金属研究总院、包头稀土研究院、钢铁研究总院、北京工业大学、燕山大学、山东大学、云南大学、上海交通大学、华中科技大学、天津大学、四川大学、湖南大学、大连理工大学、南京大学、清华大学、西南师范大学、北京科技大学、北京大学、厦门大学、中南大学、电子科技大学、重庆大学、福州大学、吉林大学、哈尔滨工业大学、武汉大学、西安理工大学、北京交通大学、西北工业大学、苏州大学、东北大学、复旦大学、武汉理工大学、浙江大学、北京理工大学、北京航空航天大学、中国科技大学、西南交通大学、南开大学、《功能材料与器件学报》编辑部、《功能材料》编辑部

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献