关于锂离子二次电池正极材料LiMn2O4高温容量衰减研究
Capacity Fade of LiMn2O4 in High Temperature for Lithiumion Rechargeable Batteries
【Author】 CHEN Zhao-yong;JIANG Qi;LIU Xing-quan;GAO Li-zhen, YU Zuo-long Research & Development Center for Functional Materials, Chengdu Institute of Organic Chemistry Chinese Academy of Sciences, Chengdu, 610041, China
【机构】 中国科学院成都有机化学研究所功能材料开发中心；
【摘要】 综述了高温下尖晶石LiMn2O4容量衰减的原因和机理。引起LiMn2O4在高温下容量衰减的原因主要可归纳为:锰的溶解;电极极化;电解液氧化;Jahn-Teller效应。其中,电极极化是高温下电池性能恶化的直接原因,但根本在于锰的溶解和电解液氧化。
【Abstract】 The reason for capacity fading and mechanism of spinel LiMn2O4 in high temperature was reviewed, and thecapacity fading was mainly caused by the dissolution of manganese, oxidation of electrolyte, and the polarization ofelectrode. The polarization of electrode was the direct reason for the deterioration of batteries, but it was caused by thedissolution of manganese and oxidation of electrolyte.
【Key words】 Spinel LiMn2O4； high temperature property； Lithium-ion rechargeable batteries；