Fe-Ni系梯度功能材料的研究
Study on Gradient Function Material of Fe—Ni Systems
【Author】 Chang Xiumin Li Yongjun Wang Shengping (Beijing General Research Institute for Non-ferrous Metals,Beijing,100088,China) Zhou Shouzeng Long Yi (University of Science and Technology,Beijng,100083,China)
【机构】 北京有色金属研究总院； 北京科技大学；
【摘要】 利用Fe、Ni粉用粒子排列法制备Ni含量从36at%到55at%连续梯度变化的Fe-Ni合金,并测出其热磁曲线。实验研究了Ni含量分别为36at%, 40ab%,45at%,50at%,55at%的五层Fe-Ni系梯度功能材料。结果表明,在实验成分范围内,随Ni含量增加,其居里温度Tc逐渐增大,多层梯度材料有与各单层相似的多个居里点Tc。成功地合成了有五个居里点的梯度功能材料。
【Abstract】 A gradient Fe-Ni multilayer alloy has been prepared by sintering the Fe-Ni mixed powders with Ni content from 36at%to 55at%in a concentration gap of 5at%per layer continually.Its thermomagnetic property has been measured.Five layers gradient function material of Fe-Ni system has been studied with Ni content being 36at%40at%45at% 50at%55at%.The results show that in the Ni concentration range of the sample for this experiment the Curie temperature(Tc) increases with the increase of Ni content,the Tc numbers agree with the layer numbers in the multilayer alloy with a Tc value in each layer similar to that of the corresponding Ni content monolayer material.The material with five Curie temperatures changing gradiently is synthesised successfully.
- 【会议录名称】 第二届中国功能材料及其应用学术会议论文集
- 【会议名称】第二届中国功能材料及其应用学术会议
- 【会议时间】1995-10-23
- 【会议地点】中国四川成都
- 【分类号】TB34
- 【主办单位】中国仪器仪表学会仪表材料学会、中国金属学会材料科学学会、中国物理学会发光分会、中国光学学会薄膜专业委员会、机械工业部重庆仪表材料研究所、《功能材料》编辑部、大连理工大学、中国科技大学、北京科技大学、吉林大学、东北大学、中国科学院上海冶金研究所、中国科学院半导体研究所、北京大学、清华大学、南京大学、华中理工大学、武汉工业大学、电子科技大学、四川联合大学、西北工业大学、北京工业大学、东南大学、青岛化工学院、北京航空航天大学、山东工业大学