机械合金化Fe60Ni40粉末的磁性能
Magnetic Properties of Mechanically Alloyed Fe60Ni40 Powders
【Author】 Yang Junyou Zhang Tongjun Cui Kun Pan Baoming (Department of Materials Science,Huazhong University of Science and Technology,Wuhan,430074,China) (+China University of Geosciences,Wuhan,430074,China)
【摘要】 本文利用行星球磨的方法研究了Fe60Ni40纯元素混合粉末的机械合金化过程,对球磨不同时间的粉末进行了XRO分析、SEM观察、显微硬度及磁性能测试。结果表明:球磨初期粉末的显微硬度、矫顽力和饱和磁感应强度随球磨时间延长而迅速增加。此后,矫顽力逐渐下降,而显微硬度和饱和磁感应强度继续上升,球磨至30h,三者都达到稳定值,延长球磨时间变化不大。
【Abstract】 Elemental powder mixture of Fe60Ni40 was mechanically alloyed in a planetary ball mill. XPD.SEM.microhardness and magnetism measurement were used to characterize the ball milled powders. It shows that the microhardness,coercivity and magnetization of powders increased rapidly with increasing milling time at the beginning of MA.When milling longer than 3h,the increasing of coercivity stopped and it turned into decreasing with the milling time,however,microhardness and magnetization kept on increasing.Prolonging milling time to 30h,all of them leveled off,and further milling would produce no evident effect on them.
【Key words】 mechanical alloying； ball milling； magnetic properties； microhardness；
- 【会议录名称】 第二届中国功能材料及其应用学术会议论文集
- 【会议名称】第二届中国功能材料及其应用学术会议
- 【会议时间】1995-10-23
- 【会议地点】中国四川成都
- 【分类号】TB383.3
- 【主办单位】中国仪器仪表学会仪表材料学会、中国金属学会材料科学学会、中国物理学会发光分会、中国光学学会薄膜专业委员会、机械工业部重庆仪表材料研究所、《功能材料》编辑部、大连理工大学、中国科技大学、北京科技大学、吉林大学、东北大学、中国科学院上海冶金研究所、中国科学院半导体研究所、北京大学、清华大学、南京大学、华中理工大学、武汉工业大学、电子科技大学、四川联合大学、西北工业大学、北京工业大学、东南大学、青岛化工学院、北京航空航天大学、山东工业大学