【作者】 马列军； 吴琦； 王海燕； 崔群；

【Author】 Liejun Ma;Q Wu;HY Wang;Q Cui;College of Chemistry and Chemical Engineering, Nanjing Tech University;

【机构】 南京工业大学化学化工学院；

【摘要】 本文采用3L的不锈钢高压反应釜为反应器,采用无HF水热合成金属有机骨架材料MIL-101,对3 MPa成型MIL-101试样(MIL-101-3-L)进行了XRD和SEM表征;用真空重量法测定MIL-101-3-L对水的吸附等温线;在TG-DTA联用热天平上测定MIL-101-3-L对水的脱附性能。结果表明,放大合成的MIL-101成型前后特征峰与晶型基本一致;吸附温度298 K时,MIL-101-3-L对水的平衡吸附量为1.10 g/g;水在MIL-101-3-L上的DTA脱附峰顶温度约为357 K;放大合成MIL-101可用于太阳能驱动的吸附制冷过程。更多还原

【Abstract】 Large scale synthesis of MIL-101 was investigated as the huge demand for adsorption refrigeration. The water adsorption and desorption performance of 3 MPa shaping amplification synthetic MIL-101-3-L was studied. Results reveal that the MIL-101-L-3 has a high water uptake of 1.10 g of water per gram of sorbent at 298 K. The desorption peak temperature is 357 K. Metal organic framework MIL-101 synthesized in large scale in this paper can be used for adsorption refrigeration powered by solar energy.更多还原