γ-TiAl合金热工艺模拟及组织研究
Study on Microstructure and Simulation on the Deformation Behavior ofγ-TiAl Alloy
【Author】 Xia CHANG1,2,Xiaobin ZHANG1,Fuhui HAN1,Jiayong SI2,Ji ZHANG2 1 Chongqing University of Technology,Chongqing,China,400050 2 Central Iron and Steel Research Institute,Beijing,China,100081
【机构】 重庆理工大学； 钢铁研究总院高温材料研究所；
【摘要】 利用Gleeble-1500型热模拟试验机对Ti-46.5Al-2.5V-1.0Cr-0.3Ni合金进行了变形温度为1000～1200℃、应变速率为0.001～1s-1的热压缩试验,根据摩擦修正后的流变应力曲线,研究了工艺参数变化对流变应力及变形组织的影响。结果表明:合金的流变应力随变形温度升高而降低,随应变速率提高而增大;合金变形后组织中动态再结晶体积分数和动态再结晶的晶粒尺寸随热压缩温度的升高而增加,随应变速率的降低而增加。
【Abstract】 The high temperature compression tests of Ti-46.5Al-2.5V-1.0Cr-0.3Ni alloy were carried on Gleeble-1500 simulator.The temperature is from 1000 to 1200℃and the strain rate is from 0.001s-1 to 1s-1.Based on the corrected stress-strain curves,the influence of processing parameters on the flow stress and the microstructure was studied.The results show that the flow stress decreases with the increase of temperature,while increase with the increase of strain rate.At the same time,the fraction and the grain size of dynamic recrystallization during the deformation rise with the increase of temperature and promote with the reduce of strain rate.
【Key words】 TiAl alloy； thermal deformation； flow stress； dynamic recrystallization；
- 【会议录名称】 2011中国功能材料科技与产业高层论坛论文集（第三卷）
- 【会议名称】加速功能材料自主创新，促进西部战略性新兴产业发展——2011中国功能材料科技与产业高层论坛
- 【会议时间】2011-11-16
- 【会议地点】中国重庆
- 【分类号】TG166.5
- 【主办单位】中国仪器仪表学会仪表功能材料学会、重庆市科学技术协会、重庆市科学技术研究院、重庆大学、重庆材料研究院（重庆仪表材料研究所）、中国人民解放军后勤工程学院、重庆功能材料期刊社、国家仪表功能材料工程技术研究中心