ZnS:Tb纳米晶的制备和光学量子效应
Preparing Nanocrystals of Tb-Doped ZnS and their Optical Quantum Effect
【Author】 Li Zhen’gang Li Lan~+ Xiong Guangnan~+ (Department of Physics,Tianjin Normal University,Tianjin,300074,China) (+ Institute of Material Physics,Tianjin Institute of Technology,Tianjin,300191,China)
【机构】 天津师范大学物理系； 天津理工学院材料物理所；
【摘要】 本文报道了一种用化学合成法在室温下制备掺铽硫化锌纳米晶的方法,制成的3种纳米晶直径分别为3.6nm,3.8nm和4.1nm,紫外吸收带边分别在282nm、288nm和295nm,相对于硫化锌体材料吸收带边的340nm有明显的蓝移。用332nm光激发的发射光谱峰值分别为548nm、547nm和546nm,表明铽已掺入ZnS纳米晶之中。
【Abstract】 We reported a chemical process for preparing ZnS nanocrystals doped with terbium activator element. The three particles of Tb-doped ZnS are estimated to be about 3.6nm,3.8nm and 4.1nm in size respectively. The ultraviolet absorptions are at 282nm,288nm and 295nm separately,which are bule shift from that expected for bandgap of bulk ZnS,340nm.The light emisson peaks of the ZnS:Tb nanocrystals are at 548nm,547nm and 546nm,with excitation energy 332nm.These are evidence that the activator Tb3+has been incorporated into the ZnS particles.
- 【会议录名称】 第三届中国功能材料及其应用学术会议论文集
- 【会议名称】第三届中国功能材料及其应用学术会议
- 【会议时间】1998-10-13
- 【会议地点】中国重庆
- 【分类号】TB383.1
- 【主办单位】中国仪器仪表学会仪表材料分会、中国金属学会功能材料分会、中国化学会、中国物理学会发光分科学会、机械工业部重庆仪表材料研究所、北京有色金属研究总院、清华大学、中国科技大学、南京大学、吉林大学、东北大学、北京科技大学、天津大学、重庆大学、四川联合大学、电子科技大学、福州大学、北京航空航天大学、湖南大学、大连理工大学、华中理工大学、北京工业大学、合肥工业大学、《功能材料》编辑部、重庆市科学技术委员会