SnO2纳米气敏材料的溶胶—凝胶法制备
Sol-Gel Preparations of Gas Sensing SnO2 Nanocrystalline Material
【Author】 Wang Yuansheng Yang Yuming~+ Huang Zhaoxin~+ Lin HuamingYang (Central Laboratory,Fuzhou University,Fuzhou,350002,China) (+ Department of Electronic Science and Applied Physics,Fuzhou University,Fuzhou,350002,China)
【机构】 福州大学中心实验室； 福州大学电子科学与应用物理系；
【摘要】 本文以无机盐为源物质,研究用不同途径的溶胶-凝胶法制备SnO2纳米晶;采用不同的制备方法得到的SnO2粉末的晶粒度各不相同,以SnCl4乙醇溶液+HCl通氨法所得到的粉末晶粒度最细,可达3.5nm;由3.5nm的SnO2粉末制备的气敏元件对H2有较好的气敏特性。
【Abstract】 Taking the inorganic salts as the source materials,some different ways of preparing SnO2 nanocrystalline powder through sol-gel processes have been studied.The average grain size of the resulted SnO2 powder in different methods were found to be different,with the finest one determined to be 3.5 nm. The gas-sensing element made from 3.5nrn powder shows quite excellent gas-sensing characters to H2.
【Key words】 sol-gel process； SnO2 nanocrystalline； gas sensing character；