EDTA络合溶胶—凝胶法制备钙钛矿型复合氧化物粉体的研究
Synthesis of Perovskite-type Oxide Powders by EDTA Complexing Sol-Gel Method
【作者】 邵宗平； 盛世善； 陈恒荣； 李林； 潘秀莲； 熊国兴；
【Author】 Shao Zongping Sheng Shishan Chen Hengrong Li Lin Pan Xiulian Xiong Guoxing (State Key Laboratory of Catalysis,Dalian Institute of Chemical Physics,Chinese Academy of Sciences,Dalian,116023,China)
【机构】 中国科学院大连化学物理研究所催化基础国家重点实验室；
【摘要】 本文报道了用EDTA络合溶胶-凝胶法合成系列的钙钛矿型复合氧化物。以LSCO(La0.8Sr0.2 CoO3)为对象对制备过程参数进行了优化。用TG-DTA, IR,XRD,SEM,QELSS等技术对制备过程、热分解机理及粉体的性质进行了研究,证明了在形成纯钙钛矿相之前锶要经过从硝酸盐到碳酸盐转化这一步。
【Abstract】 A series of perovskite-type composite oxides were synthesized by the EDTA complexing sol-gel method,The formation process of LSCO(La0.8Sr0.2CoO3)was investigated by TG-DTA,XRD and FTIR spectroscopy,in the process of forming perovskite LSCO,SrCO3 was occurred and calcination temperature higher than 800℃was needed to get rid of it.The BET area of the as-prepared powder（LSCO）is about 10m2/g,larger than that prepared by standard ceramic method.
- 【会议录名称】 第三届中国功能材料及其应用学术会议论文集
- 【会议名称】第三届中国功能材料及其应用学术会议
- 【会议时间】1998-10-13
- 【会议地点】中国重庆
- 【分类号】TB383.4
- 【主办单位】中国仪器仪表学会仪表材料分会、中国金属学会功能材料分会、中国化学会、中国物理学会发光分科学会、机械工业部重庆仪表材料研究所、北京有色金属研究总院、清华大学、中国科技大学、南京大学、吉林大学、东北大学、北京科技大学、天津大学、重庆大学、四川联合大学、电子科技大学、福州大学、北京航空航天大学、湖南大学、大连理工大学、华中理工大学、北京工业大学、合肥工业大学、《功能材料》编辑部、重庆市科学技术委员会