Ti、Ta和C注入后碳钢抗腐蚀特性研究

Study of Corrosion Resistance for Ti,Ta or C Implanted Carbon Steel

推荐 CAJ下载
PDF下载
不支持迅雷等下载工具，请取消加速工具后下载。

【Author】 Ma Furong Deng Zhiwei Zhang Tonghe (Institute at Low Energy Nuclear Physics,Beijing Normal University,Beijing,100875,China)

【机构】北京师范大学低能核物理研究所；

【摘要】我们对MEVVA强流金属离子注入Ti、Ta和C的碳钢的抗腐蚀特性进行了研究和比较。结果表明,经过Ta、C+Ta注入的碳钢的腐蚀电流密度比未经注入的碳钢降低了56%～26%,经过Ti、C+Ti注入的碳钢的腐蚀电流密度比未经注入的碳钢降低了72%～11%。离子注入形成碳或铁的弥散相分布于碳钢表层构成抗腐蚀结构,从而提高了基体的抗腐蚀性能。更多还原

【Abstract】 The behavior of weak acid corrosion resistance was studied for Ti,Ta or C implanted carbon steel by MEVVA ion source.The results showed that the corrosion current density of ion implanted carbon steel was much smaller than that of unimplanted one.The peak density of corrosion current for C₄ or C₄Ti₄ decreased 70%compared with that for carbon steel and the best properties of corrosion resistance could be got while suitable doses were given.更多还原

【关键词】抗腐蚀； EVVA源；强流金属离子注入碳钢；
【Key words】 corrosion resistance； MEVVA ion source； high-current metal ion implanting； carbon steel；

【会议录名称】第三届中国功能材料及其应用学术会议论文集

【会议名称】第三届中国功能材料及其应用学术会议

【会议时间】1998-10-13
【会议地点】中国重庆
【分类号】TG174.3

【主办单位】中国仪器仪表学会仪表材料分会、中国金属学会功能材料分会、中国化学会、中国物理学会发光分科学会、机械工业部重庆仪表材料研究所、北京有色金属研究总院、清华大学、中国科技大学、南京大学、吉林大学、东北大学、北京科技大学、天津大学、重庆大学、四川联合大学、电子科技大学、福州大学、北京航空航天大学、湖南大学、大连理工大学、华中理工大学、北京工业大学、合肥工业大学、《功能材料》编辑部、重庆市科学技术委员会

知网节下载

节点文献中：

本文链接的文献网络图示:

本文的引文网络

节点文献