还原氮化法制备立方氮化铝陶瓷粉末的研究
Synthesis of Cubic Aluminum Nitride by Carbothermal Nitriding Reaction
【Author】 Wang Jian Ding Peidao Yang Yuanxin Wang Wanlu~+ (Department of Metallurgy and Materials Engineering, Department of Applied Physics,Chongqing University,Chongqing,400044,China)
【机构】 重庆大学冶金及材料工程系； 重庆大学应用物理系；
【摘要】 采用氧化铝还原氮化法,研究制备立方AlN陶瓷粉末。研究原料粉末特性、还原氮化温度及保温时间等对立方AlN合成的影响;并分析了立方AlN的生成机理和存在规律。结果表明,降低Al2O3粉末粒度可降低立方AlN的生成和存在温度;在立方AlN已经生成的条件下,随反应温度提高和反应时间延长,立方AlN会转变为六方AlN;立方AlN为一高温不稳定相,在1800℃左右转变为六方AlN;立方AlN可能是Al2O3与六方AlN反应生成的Al23O27N5的反应产物。
【Abstract】 The cubic aluminum nitride（AlN）powder was synthesized by carbothermal nitriding reaction of aluminum oxide（Al2O3）.The effects of Al2O3 particle size,reactive temperature and reactive time on cubic AlN synthesis were investigated.The reaction mechanism also was analyzed.The results showed that cubic AlN is formed at lower temperature in fine Al2O3 powder than that in coarse Al2O3 powder.The cubic AlN could be the the product of Al23O27N5 synthesized by Al2O3 and wurtzite AlN,and transforms into wurtzite AlN above 1800℃.
【Key words】 cubic aluminum nitride； carbothermal intruding reaction； ceramic powder；