新型镍电极材料——高密度球形微粒Ni（OH）2Ⅱ微米粒子Ni（OH）2晶粒的纳米尺寸和电化学性能
New Type Nickel Electrode Material—High Density Spherical Particle Ni（OH）2 Ⅱ Electrochemical Performance Nanosize of Ni（OH）2 Crystalline Grain with Micro Grade
【Author】 Zhao Linzhi Yang Shuting Zhao Peizheng Ding Li Zhang Mingchun (Department of Chemistry,Henan Normal University,Xinxiang,453002,China)
【机构】 河南师范大学化学系；
【摘要】 固定主要添加剂,以Ni（NO3）2或NiSO4溶液、氨水和NaOH溶液为原料液,在特殊结构反应器中,调整和控制不同的反应条件可制备出不同物理和结晶学参数的球形Ni（OH）2样品。选出五种有代表性的样品进行结构和物理性能测试,制成镍正极与储氢合金负极组成AA型MH/Ni电池并进行电化学容量和性能测试,得到一些规律性的东西,似乎说明钴等掺杂增加标准容量,微观结构影响放电平台和高倍率性能。
【Abstract】 Using the solution of Ni（NO3）2 or NiSO4,NH3·H2O and NaOH as the original solution,adjusting and controlling the different conditions of reaction in the reaction vessel with special structure.The spherical Ni（OH）2 sample with different physical and crystalline parameter was prepared by fixing main dopants.The structure and physical properties for theselected five samples which is typical representative was measured.The electrochemical capacity and performnce of the AA-MH/Ni battery which was made up with above sample as cathodee and metal Hydride as anode was also measured.The some laws from the measurement shown that the standard capacity of cathode was increased by doping Co and discharge plate and the high multiplier property was related to the microstructure of the sample.
【Key words】 Spherical Ni（OH）2； methode of preparation； microstructure； electrochemical properties；