SrFeCo0.5Ox混合导体材料电导性质的研究
Ionic and Electronic Conductivity Properties of SrFeCo0.5Ox
【Author】 Zhang Yahong Jiang Yi Wang Shizhong Yan Jingwang Li Wenzhao (Dalian Institute of Chemical Physics,Chinese Academy of Sciences,Dalian,116023,China)
【机构】 中国科学院大连化学物理研究所；
【摘要】 采用电子隔离法测定了SrFeCo0.5Ox混合导体材料的氧离子电导,研究了该材料的总电导、离子电导、电子电导随反应温度及氧分压的变化规律。SrFeCo0.5Ox具有较高的电导率及氧离子迁移数,在1123K总电导率为8.4S·cm-1,离子迁移数约为0. 5。在氧分压1.5Pa 101kPa范围内SrFeCo0.5Ox材料的电导主要受间隙氧离子及电子空穴影响。该材料的性质受氧分压及反应温度的影响较大,在不同条件下表现出不同的性质。
【Abstract】 The ionic conductivity of SrFeCo0.5Ox was measured with electron-blocking electrodes.The total, electronic,and ionic conductivities have been investigated as a function of temperature and oxygen pressure. SrFeCo0.5Ox exhibits high total conductivity as well as a high transference number.At 1123K,the total conductivity and the transference number of SrFeCo0.5Ox is 8.4 S·cm-1 and 0.5 respectively,which demonstrates that SrFeCo0.5Ox is a real mixed conductor.Within the oxygen partial pressure and temperature range employed（101kPa～1.5Pa,1023K～1223K）,the predominant defects that affect the material conductivities are interstitial oxygen ions and electron holes.The electrode properties of SrFeCo0.5Ox are greatly influenced by temperature and oxygen partial pressure,and may change significantly under different experimental conditions.
【Key words】 mixed conductor； ionic conductivity； electronic conductivity； electron-blocking electrode； transference number；