BaSn0.1Ti0.9O3·yLa2O3纳米粉的合成、烧结与介电特性
Synthesis,Sintering and Dielectric Characterization of BaSn0.1 Ti0.9O3·yLa2O3 nm-powder
【作者】 丁士文； 翟永清； 王志强； 李金龙； 李颖； 陈静；
【Author】 Ding Shiwen Zhai Yongqing Wang Zhiqing Li Jinlong Li Ying Chen Jing (Department of Chemistry,Hebei University,Baoding,071002,China)
【机构】 河北大学化学系；
【摘要】 采用软化学方法在100℃以下水溶液中合成出了一系列BaSn0.1 Ti0.9O3·yLa2O3（0≤y≤0.04）固溶体纳米粉末。测定了不同温度和不同时间所烧结的陶瓷体的介电常数。找出了最佳烧结时间和烧结温度分别为2h和1200℃。对不同组成固溶体的介电特性进行了研究,结果表明,用化学方法在BaTiO3中掺入适量锡和镧后,引起Tc前移,室温介电常数提高,最高可达38000以上。
【Abstract】 A series of BaSn0.1Ti0.9O3·yLa2O3 solid solations with an average particle diameter of 60 nm were synthesized by means of soft chemical method and the sinterring temperature and time were studied.The result of test showed that adulterating with tin and lanthanum in pure BaTiO3 phase obviously improved the dielectric constant at normal temperature.When the amount of tin and lanthanum adulterated were 0.1 and 0. 002 respectivily,the ceramic body thus produced has a dielectric constant up to 38000.The sinterring temperature and time of ceramic body were 1200℃and 2h respectively.
【Key words】 BaTiO3 solid solation； sinterring； dielectric characterization；