不同表面处理工艺对快淬NdFeB永磁粉抗氧化性影响
The Effect of Different Surface Treatment Processes on the Oxidation Resistance of Rapidly Ouenching NdFeB Magnetic Powder
【Author】 Liu Yin Chen Yue Tu Mingjing (Department of Metal Material,Sichuan Union University Chengdu,Chengdu,610065,China)
【机构】 四川联合大学金属材料系；
【摘要】 本文对快淬NdFeB永磁粉分别采用化学镀镍、重铬酸盐钝化处理、重铬酸盐钝化还原处理,以及硅烷偶联处理和重铬酸盐钝化—还原/硅烷复合处理等工艺进行了表面包覆,研究了表面包覆处理前后的快淬NdFeB磁粉的抗氧化特性,结果表明上述工艺方法均能改善NdFeB磁粉的抗氧化性,其中以重铬酸盐钝化—还原/硅烷偶联处理形成的包覆层的抗氧化性最佳。
【Abstract】 This paper presents the oxidation resistance of rapidly quenching Nd-Fe-B before and after the surface treatment by ellectricless nickel,dichromate passivating treatment,dichromate passivating and reducting treatment,silane aginng treatment,and dichromate passivating and reducting and silane aging compound treatment.The results show that all the method of processes can improve the oxidattion resistance of rapidly qquenching Nd-Fe-B magnetic powder,especially the oxidation resistance of rapidly quenching with the coating by the dichromate passivating and reducting and silane aging compound treatment.
【Key words】 rapidly quenching Nd-Fe-B magnetic powdr； surface treatment； oxidation resistance；