锌/铁/二氧化硅复合电镀工艺研究
Study on Zn/Fe/SiO2 Composite Electrodoposition
【Author】 Fan Yunying, Zhang Yingjie, Dong Peng (Kunming University of Science and Technology, Kunming, 650093)
【机构】 昆明理工大学；
【摘要】 分别采用硫酸盐体系和氯化物体系的最佳工艺条件电沉积制备了高铁(Femass%>1%)和低铁(Femass%<1%)的Zn-Fe-SiO2复合镀层,并系统测试了不同厚度Zn-Fe-SiO2复合镀层的耐蚀性、结合力、孔隙率和氢脆性等综合性能,同时与电镀Zn及Zn-Fe合金进行了对比。实验结果表明:Zn-Fe-SiO2复合镀层无需钝化,其耐蚀性及其它综合性能均优于Zn-Fe合金镀层和Zn镀层。因此,相对于电镀Zn及Zn-Fe合金,电沉积Zn-Fe-SiO2复合镀层技术具有先进性,应用前景良好。
【Abstract】 High-iron(Fe mass%>1%)and low-iron(Fe mass%<1%)Zn-Fe-SiO2 composite coatings were obtained from sulfate bath and chloride bath with optimum technics. Corrosion resistance, adhesion, porosity and hydrogen embrittlement of Zn-Fe-SiO2 composite coatings were tested systematically, and these data was compared with the properties of Zn and Zn-Fe alloy. The results show that corrosion resistance and all other properties of Zn-Fe-SiO2 composite coatings are better than Zn and Zn-Fe alloy’s. Therefore, the Zn-Fe-SiO2 composite electrodepositing technique is superior to Zn and Zn-Fe alloy electroplating , with a great future in application.
【Key words】 composite coating； corrosion resistance； adhesive； porosity； hydrogen embrittlement；
- 【会议录名称】 第15届全国腐蚀与表面保护技术研讨会暨首届全国腐蚀与表面保护技术青年论坛论文集
- 【会议名称】第15届全国腐蚀与表面保护技术研讨会暨首届全国腐蚀与表面保护技术青年论坛
- 【会议时间】2009-05
- 【会议地点】中国浙江宁波
- 【分类号】TQ153.2
- 【主办单位】中国腐蚀与防护学会涂料涂装及表面保护专业委员会、中国腐蚀与防护学会青年工作委员会、中国机械工程学会表面工程分会