【摘要】 以苯酚和松节油为原料，通过调节二者比例制备了4种萜烯酚树脂；以丙烯酸异辛酯(EHA)、丙烯酸丁酯(BA)、丙烯酸甲酯(MA)为单体通过溶液聚合制备了不同的聚丙烯酸酯；将4种萜烯酚树脂分别加入不同的聚丙烯酸酯中，考察不同共混物相容性和粘接性能的差异。研究结果表明，随着苯酚用量增加，萜烯酚树脂的极性先增大后基本保持不变；极性较小的萜烯酚树脂与聚丙烯酸酯相容性更佳；萜烯酚树脂对聚丙烯酸酯的粘接性能有所提高，但是对其润湿性能有负面影响。更多还原

【Abstract】 Four kinds of terpene phenol resins are prepared by adjusting the ratio of phenol to turpentine.Different polyacrylate are prepared via solution polymerization using 2-ethylhexyl acrylate(EHA),butyl acrylate(BA) and methyl acrylate(MA) as raw materials.Four kinds of terpene phenol resins are separately added into different polyacrylate, and the differences in compatibility and adhesion properties of different blends are studied.Study results show that the polarity of terpene phenol resin increases firstly and then remains basically unchanged with the increase of phenol dosage.The terpene phenol resin with less polarity has better compatibility with polyacrylate.The adhesion property of polyacrylate is improved due to blending with terpene phenol resin, but the wettability is negatively affected.更多还原