【摘要】 2022年，法国电力公司（EDF）大量核电机组因一回路管道应力腐蚀开裂（SCC）问题而停堆检修，对法国甚至欧洲的生产生活造成巨大影响。针对该事件，在总结国内外核反应堆类似失效案例及材料老化研究成果的基础上，对反应堆不锈钢部件的SCC问题的机理、影响因素、抑制措施开展了分析，并结合我国核电机组服役时间逐渐延长，材料老化、设备失效问题日益突出的现状，提出我国核电运维改进措施，如优化残余应力、加强监督和检查，研发更有效的无损检测技术等。同时，探讨了我国在反应堆材料老化研究方面的发展方向。更多还原

【Abstract】 In 2022, a large amount of EDF nuclear power plants(NPP) were shut down because of stress corrosion crack(SCC) on primary pipe of reactor. It led enormous impact on industry and normal life in France and Europe. To understand this accident, the mechanism, effect factors and migration methods of SCC were analyzed on the basis of summarizing similar failure cases and material aging research results of nuclear reactors at home and abroad. Combined with the increasingly prominent problems such as the gradual extension of the service time, the aging of materials and equipment failure of nuclear power units in China, mitigation measures such as reduction of residual stress, improvement of inspection and development of advance nondestructive examination technologies were suggested. Also, the development direction of aging research on reactor materials in China was discussed.更多还原