【摘要】 针对接触条件对电连接器热插拔条件下性能影响不明的问题，采用H62/T2弹性接触摩擦副，在微-滑动摩擦试验机上，对其进行往复滑动载流摩擦实验，研究了接触面积对H62/T2载流摩擦磨损性能的影响。结果表明：在给定电流为2 A、4 A、6 A条件下，随接触面积的增加，摩擦系数波动性降低，即摩擦过程的稳定性提高，平均摩擦系数和总磨损体积均呈现增大趋势；在电流为2 A条件下，当圆弧半径从1.5 mm增加至5.5 mm时，电流波动性减小，载流稳定性提高，载流效率η从98.26%提高至99.73%。摩擦副的摩擦磨损机制包括磨粒磨损、粘着磨损、电弧侵蚀且多机制耦合作用，随接触面积的增加，以熔融和喷溅为主的电弧侵蚀减少，以犁沟和粘着为主的机械磨损加剧。更多还原

【Abstract】 Aiming at the problem that the influence of contact conditions on the performance of electrical connectors under the contact hot-swap plug condition was unclear, the H62 wire/T2 plate elastic contact friction pair was used to carry out reciprocating sliding current-carrying friction experiments on the micro-sliding friction testing machine, and the influence of contact area on the friction and wear performance of H62/T2 current-carr-ying was studied. The experimental results show that under the condition of a given current of 2 A, 4 A and 6 A, with the increase of contact area, the friction coefficient stability parameter ε decreases, that is, the stability of the friction process increases, and the average friction coefficient and wear volume show an increasing trend. Under the condition of current of 2 A, when the arc radius increases from 1.5 mm to 5.5 mm, the current fluctuation decrease, the current carrying stability increase, and the current carrying efficiency increases from 98.26% to 99.73%. The wear of the friction pair presents the form of abrasive wear, adhesive wear and arc erosion coexisting and coupling, with the increase of contact area, arc erosion decreases, and mechanical wear is intensified by furrow and adhesion.更多还原