田口实验设计法优化碳酸锂反应结晶制备工艺

Optimizing preparation process of lithium carbonate reaction crystallization by Taguchi experimental design method

  • 推荐 CAJ下载
  • PDF下载
  • 不支持迅雷等下载工具,请取消加速工具后下载。

【作者】 王斌邓小川史一飞董超超樊发英朱朝梁樊洁马婉霞左方涛

【Author】 Wang Bin;Deng Xiaochuan;Shi Yifei;Dong Chaochao;Fan Faying;Zhu Chaoliang;Fan Jie;Ma Wanxia;Zuo Fangtao;Key Laboratory of Comprehensive and Highly Efficient Utilization of Salt Lake Resources,Qinghai Institute of Salt Lakes,Chinese Academy of Sciences;Qiughai Engineering and Technology Research Center of Comprehensive Utilization of Salt Lake Resources;University of Chinese Academy of Sciences;Yinchuan Branch of State Power Science & Research Institute Co.,Ltd.;

【通讯作者】 邓小川;

【机构】 中国科学院青海盐湖研究所中国科学院盐湖资源综合高效利用重点实验室青海省盐湖资源综合利用工程技术中心中国科学院大学国家能源集团科学技术研究院有限公司银川分公司

【摘要】 单因素实验无法全面、可靠地研究各因素对反应结晶过程制备高品质碳酸锂的影响,田口设计有利于全面研究各因素对制备高品质碳酸锂的影响,实验周期较短,实验成本较低。以东台吉乃尔盐湖精制卤水为原料,设计田口实验,采用聚焦光束反射测量仪FBRM G400实时在线研究反应温度、搅拌速率、卤水加料速度、碳酸钠浓度等因素对反应结晶工艺中碳酸锂粒径和纯度的影响。通过田口实验表明搅拌速率对碳酸锂的粒径影响最大,碳酸锂的纯度对反应温度最敏感。研究结果表明,反应温度为85℃、搅拌速率为200 r/min、卤水加料速度为2 mL/min、碳酸钠质量浓度为201.6 g/L时得到的碳酸锂品质最优,其粒度为3.71μm,纯度高达99.62%。

【Abstract】 Single-factor experiment cannot comprehensively and reliably study the influence of various factors on the preparation of high-quality lithium carbonate during the reaction crystallization process.Taguchi′ s design is conducive to the comprehensive study of various factors to prepare high-quality lithium carbonate.The experiment cycle is shorter and the experiment cost is lower.Using the refined brine of Dongtai Jinel Salt Lake as the raw material,Taguchi experiment was designed,and the focused beam reflection measuring instrument FBRM G400 was used to study effect of the reaction temperature,stirring rate,brine feed rate,Na2CO3 concentration and other factors on the reaction crystallization process in real-time on-line study of the lithium carbonate particle size and purity.Taguchi experiments showed that the stirring rate had the greatest influence on the particle size of lithium carbonate,and the purity of lithium carbonate was most sensitive to the reaction temperature.The results of the study showed that when the reaction temperature was 85 ℃,the stirring rate was 200 r/min,the brine feed rate was 2 mL/min,and the mass concentration of Na2CO3 was 201.6 g/L,the quality of obtained lithium carbonate was the best with particle size of 3.71 μm and purity of 99.62%.