【摘要】 采用X射线衍射仪（XRD）,振动样品磁强计（VSM）,电化学工作站以及扫描电子显微镜（SEM）等试验仪器对辊速为14.65和43.96 m/s旋淬制备的Fe_73.5Si_13.5B₉Cu₁Nb₃（C1和C2）合金条带进行了测试分析。XRD结果显示,低冷速下制备获得了非晶/纳米晶双相（C1）合金,高冷速制备的合金（C2）为非晶态。VSM结果显示,C1和C2合金均具有优异的软磁性能。低冷速制备的纳米晶（C1）合金相比高冷速制备的非晶态（C2）合金具有较强的磁各向异性,C1合金磁各向异性的增强是由纳米晶相的键对有序性以及纳米晶相与非晶基体相互作用引起的磁弹各向异性所致。合金的电化学测试显示,C2合金耐腐蚀性能要好于C1合金,合金耐腐蚀性能的差异与制备过程中不同冷速所导致的合金表面组织结构和应力不均匀性相关。更多还原

【Abstract】 The Fe_73.5Si_13.5B₉Cu₁Nb₃ alloy ribbons fabricated at circumference speed of 14.65 and 43.96 m/s（labeled as C1 and C2） were investigated by XRD, VSM, electrochemical workstation and SEM. The XRD results show that the low-cooling-rate sample（C1） has a nanocrystalline/amorphous dual-phase structure and the high-cooling-rate sample（C2） has an amorphous structure. VSM results show that both C1 and C2 alloys have excellent soft magnetic properties, and C1 alloy shows a strong magnetic anisotropy, which is induced by both the ordered atomic bonds of nanocrystalline phase and strong interaction between the nanocrystalline phase and amorphous matrix. The electrochemical polarization test results show that the corrosion resistance property of C2 alloy is better than that of C1 alloy, which is attributed to the heterogeneity structure and internal stress in the ribbon surface formed on the spinning process.更多还原