【摘要】 We report the successful synthesis of a new diluted magnetic semiconductor（Ca,Na）（Zn,Mn）₂Sb₂. Na and Mn are doped into the parent compound CaZn₂Sb₂, which has the same crystal structure as that of "122" type iron-based superconductor CaFe₂As₂. Na substitution for Ca and Mn substitution for Zn introduce carriers and spins, respectively. Doping Mn atoms alone up to 5% does not induce any type of magnetic ordering. When both Na and Mn are co-doped, a ferromagnetic ordering with maximum T_C～ 10 K has been observed. Iso-thermal magnetization shows that the coercive field is up to ～ 245 Oe at 2 K. Below T_C, a negative magneto-resistance with MR ～ 12% has also been achieved.更多还原

【Abstract】 We report the successful synthesis of a new diluted magnetic semiconductor（Ca,Na）（Zn,Mn）₂Sb₂. Na and Mn are doped into the parent compound CaZn₂Sb₂, which has the same crystal structure as that of "122" type iron-based superconductor CaFe₂As₂. Na substitution for Ca and Mn substitution for Zn introduce carriers and spins, respectively. Doping Mn atoms alone up to 5% does not induce any type of magnetic ordering. When both Na and Mn are co-doped, a ferromagnetic ordering with maximum T_C～ 10 K has been observed. Iso-thermal magnetization shows that the coercive field is up to ～ 245 Oe at 2 K. Below T_C, a negative magneto-resistance with MR ～ 12% has also been achieved.更多还原