【摘要】 在不同温度（650,700℃）和压力为27 MPa的蒸汽中对锅炉管用Sanicro25奥氏体耐热钢进行不同氧化时间（200,500,800,1 300,2 000h）的氧化试验,研究了试验钢表面及截面形貌、表面物相组成和氧化行为。结果表明:随着温度升高和氧化时间延长,试验钢表面氧化膜的厚度均增大,抗蒸汽氧化性能降低;在不同温度氧化2 000h后,试验钢表面氧化膜内层为（Ni,Fe）Cr₂O₄和Cr₂O₃,外层为Fe₃O₄,在700℃下内层和外层还分别含有Cr_1.3Fe_0.7O₃和（Ni,Fe）Cr₂O₄,试验钢表面均生成连续致密的氧化膜。更多还原

【Abstract】 Steam oxidation tests were conducted on Sanicro25 heat resistant austenitic steel for boiler tube under 27 MPa at different temperatures（650,700℃）for different oxidation times（200,500,800,1 300,2 000 h）.The surface and cross section morphology,surface phase composition and oxidation resistance of the test steel were studied.The results show that with the temperature and oxidation time increasing,the thickness of oxide film on the surface of test steel increased,and the steam oxidation resistance decreased.After oxidation at different temperatures for 2 000 h,the inner layer of the oxide film on surface of the test steel was composed of（Ni,Fe）Cr₂ O₄ and Cr₂O₃,and the outer layer was composed of Fe₃O₄;while at 700℃,the inner and outer layers contain Cr_1.3Fe_0.7O₃ and（Ni,Fe）Cr₂ O₄,respectively.A dense and continuous oxide film was formed on the surface of the test steel.更多还原