通过控制结晶法制备类球形Ni_(0.9)Co_(0.05)Al_(0.03)Zr_(0.02)(OH))2前驱体,与LiOH·H_2O均匀混合后,在750℃下于氧气中进行高温焙烧,最终合成正极材料Li(Ni_(0.9)Co_(0.05)Al_(0.05))O_2。扫描电子显微镜(SEM)结果显示前驱体及正极材料具有良好的形貌;X射线衍射(XRD)表明材料具有规整的六方单相层状α-Na FeO_2结构;能谱仪(EDXS)分析表明Zr元素在材料颗粒内部呈均匀分布。合成的Ni_(0.9)Co_(0.05)Al_(0.03)Zr_(0.02)O_2正极材料具有良好的电化学性能,在25℃,2.8~4.3 V充放电条件下,0.2C首次放电比容量为221.5 m Ah·g-1,充放电效率90.3%,2C倍率充放电条件下容量仍达到192.7 m Ah·g-1,100周循环后的容量保持率为92.2%。在55℃,2.8~4.3 V的高温充放电条件下,该材料的0.2C首次放电比容量可达236.2 m Ah·g-1,2C充放电倍率下循环100周容量保持率为85.1%。
【英文摘要】
Spherical precursor Ni_(0.9)Co_(0.05)Al_(0.03)Zr_(0.02)(OH)_2 was obtained by controlled crystallization method. A uniform mixture of Ni_(0.9)Co_(0.05)Al_(0.03)Zr_(0.02)(OH)2 and Li OH·H_2O was sintered under 750 ℃ in O_2 atmosphere to synthesize layered Li(Ni_(0.9)Co_(0.05)Al_(0.03)Zr_(0.02))O_2 cathode material. SEM images show that the precursor and cathode material have well morphology. XRD patterns show that the product possesse a well-layered α-Na FeO_2 structure. EDXS images show the Zr element in th...
【基金】
国家自然科学基金(No.51602352)资助项目
【更新日期】
2018-04-28
【分类号】
TM912
【正文快照】
0引言锂离子电池正极材料正朝着高容量、低成本和高安全性能的方向发展[1-4],目前商业化的锂离子电池正极材料仍以Li Co O2为主,具有层状六方α-Na Fe O2结构的Li Ni1-xCoxO2(0
| 
推荐 
点击下列相关研究机构和相关文献作者，可以直接查到这些机构和作者被《中国知识资源总库》收录的其它文献，使您全面了解该机构和该作者的研究动态和历史。