【摘要】 在碳化硅粉中添加质量分数为1%~5%的石墨烯,采用无压烧结工艺在2 190℃保温1h制备石墨烯/碳化硅陶瓷复合材料,研究了石墨烯添加量对复合材料物相组成、密度和力学性能的影响。结果表明:该复合材料由碳化硅相及少量石墨相组成;随着石墨烯添加量的增加,复合材料的密度下降,相对密度变化较小,抗弯强度和断裂韧度先增大后减小,硬度下降;当石墨烯的质量分数为3%时,复合材料的抗弯强度为395 MPa、硬度为89HRA、断裂韧度为6.0 MPa·m1/2,综合力学性能最好。更多还原

【Abstract】 Graphene/silicon carbide ceramic composites were prepared by pressureless sintering silicon carbide powders with addition of 1 wt%-5 wt% graphenes at 2 190 ℃ for 1 h.The effects of graphene addition amount on the phase composition,density and mechanical properties of the composite were studied.The results show that the composite was composed of silicon carbide phase and small amount of graphite phase.With the increase of graphene addition amount,the density of the composite decreased,the relative density changed little,the bending strength and fracture toughness increased first and then decreased,and the hardness decreased.When the mass fraction of graphene was 3%,the bending strength of the composite was 395 MPa,the hardness was 89 HRA and the fracture toughness was 6.0 MPa·m1/2;the comprehensive mechanical properties were the highest.更多还原