Investigation on the Formation Mechanism of Ordered Carbide （FeMn）₃AlC in the Al Added Twinning-Induced Plasticity Steels

【摘要】 The spinodal composition zone in Al added Fe-Mn-Al-C twinning-induced plasticity（TWIP） steels can be determined by contents of Al and C and aging temperature together, based on the thermodynamic analysis. Precipitation of ordered（FeMn）₃AlC carbide by the mechanism of spinodal decomposition occurs in the C-rich and Al-rich zone with low aging temperature. Increase of aging temperature shrinks spinodal composition zone to the high Al and C contents. As a result, the precipitation of（FeMn）₃AlC carbide alters from spinodal decomposition to classical nucleation-growth manner gradually. Further calculation indicates that the diffusion of Al can play a key role in determining the growth rate of（FeMn）₃AlC carbide at high aging temperature.更多还原

【Abstract】 The spinodal composition zone in Al added Fe-Mn-Al-C twinning-induced plasticity （TWIP） steels can be determined by contents of Al and C and aging temperature together, based on the thermodynamic analysis. Precipitation of ordered （FeMn）₃AlC carbide by the mechanism of spinodal decomposition occurs in the C-rich and Al-rich zone with low aging temperature. Increase of aging temperature shrinks spinodal composition zone to the high Al and C contents. As a result, the precipitation of（FeMn）₃AlC carbide alters from spinodal decomposition to classical nucleation-growth manner gradually. Further calculation indicates that the diffusion of Al can play a key role in determining the growth rate of（FeMn）₃AlC carbide at high aging temperature.更多还原