Preparation and Electrochemical Application of Praseodymium Modified TiO₂-NTs/SnO₂-Sb Anode by Cyclic Voltammetry Method

【摘要】 A Pr-doped TiO₂-NTs/SnO₂-Sb electrode was prepared by a simple method, cyclic voltammetry（CV）. The methyl orange（MO）aqueous solution was selected as a simulated wastewater. The ordered microstructural TiO₂-NTs substrate was synthesized by an electrochemical method to obtain large specific surface area and high space utilization. The phase structure, electrode surface morphology and electrochemical properties of electrodes were characterized by XRD, SEM and electrochemical technology, respectively. The results showed that praseodymium oxide was successfully doped into the SnO₂-Sb film by CV method. Due to the doped Pr, the oxygen evolution potential increased from 2.25 V to 2.40 V. The degradation of MO was investigated by UV-vis. The C_t /C₀（φ）was studied as a function to obtain the optimal parameters, such as the amount of doped Pr, current density and initial dye concentration. In addition, the degradation process followed pseudo-first-order reaction kinetics and the rate constant was 0.0993 min^-1. The result indicated that the introduction of Pr reduced the formation of oxygen vacancies or enhanced the formation of adsorbed hydroxyl radical groups on the surface, thus leading to better activity and stability.更多还原

【Abstract】 A Pr-doped TiO₂-NTs/SnO₂-Sb electrode was prepared by a simple method, cyclic voltammetry（CV）. The methyl orange（MO）aqueous solution was selected as a simulated wastewater. The ordered microstructural TiO₂-NTs substrate was synthesized by an electrochemical method to obtain large specific surface area and high space utilization. The phase structure, electrode surface morphology and electrochemical properties of electrodes were characterized by XRD, SEM and electrochemical technology, respectively. The results showed that praseodymium oxide was successfully doped into the SnO₂-Sb film by CV method. Due to the doped Pr, the oxygen evolution potential increased from 2.25 V to 2.40 V. The degradation of MO was investigated by UV-vis. The C_t /C₀（φ）was studied as a function to obtain the optimal parameters, such as the amount of doped Pr, current density and initial dye concentration. In addition, the degradation process followed pseudo-first-order reaction kinetics and the rate constant was 0.0993 min^-1. The result indicated that the introduction of Pr reduced the formation of oxygen vacancies or enhanced the formation of adsorbed hydroxyl radical groups on the surface, thus leading to better activity and stability.更多还原